PHYSICAL  PROPERTY  TEST DATA

 

Material N7001               Color :BLACK       Date :20070201                     

Press Cure   Sheet:  6   min  170          Button:  30   min 160     O-ring:      S      

Post Cure    Sheet:      min               Button:     min           O-ring:      S      

Customer                                    TEL:0592-6313227         FAX:0592-6313223

 

SPECIFICATION:   ASTMD2000  M2BG714A14B14EA14EF11EF21EO14EO34F17
* ITEM

REQUIRED

TEST DATA

* Original Property

Hardness,  Pts  SHOREA

   70+/-5

      72

Specific Gravity ,  g/cm3

  

1.24

Modulus ,     %

 

 

Tensile strength 

    14Mpa

    15.4Mpa

Elongation,  %

     250

      380

* A14  Heat Aged ,  ASTM  D 573    70  Hrs  at  100

Hardness Change ,  Pts

    +/-15

+3

Tensile Strength Change ,  %

    +/-30

+5.1

Elongation Change ,  %

     -50

-26.7

* B14 Compression Set , ASTM D395  Method B    22 Hrs  at 100

Deflection ,  %  ( button)

     25

7.5

*Z  O-ring  Compression Set, ASTM D1414   _______Hrs  at _____

Deflection ,  %

 

 

C  Ozone Resistance,    pphm     h  at    

 

 

*EA14  Water Resistance , ASTM  D471     70 Hrs  at  100

Hardness Change ,  Pts

       +/-10

-3.6

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

       +/-15

+9.5

*EF 11  Fluid Resistance, Ref. Fuel A , ASTM  D471    70  Hrs  at 23

Hardness Change ,  Pts

+/-10

-3

Tensile Strength Change ,  %

-25

-8

Elongation Change ,  %

-25

-13.4

Volume Change ,  %

-5~+10

+2.2

*EF 21  Fluid Resistance, Ref. Fuel B , ASTM  D471     70  Hrs  at 23

Hardness Change ,  Pts

-30~0

-12

Tensile Strength Change ,  %

-60

-29.1

Elongation Change ,  %

-60

-25.6

Volume Change ,  %

0~+40

+21.9

*EO14  Fluid Resistance, ASTM # 1 oil ,  ASTM  D471   70 Hrs  at 100

Hardness Change ,  Pts

-5~+10

+5

Tensile Strength Change ,  %

-25

+7.4

Elongation Change ,  %

-45

-28.7

Volume Change ,  %

-10~+5

-6.4

*EO34  Fluid Resistance, ASTM # 3 oil ,  ASTM  D471    70  Hrs  at 100

Hardness Change ,  Pts

-10~+5

-5

Tensile Strength Change ,  %

-45

+3.8

Elongation Change ,  %

-45

-22.6

Volume Change ,  %

0~+25

+7.6

*F17 Low-temperature nonbrittle after 3min at -40

 

PASS

Engineer:_____                    Plant Manager: ______

 

XIAMEN HAIYIXIN RUBBER SEAL CO.,LTD  

                                                                                                      

           PHYSICAL  PROPERTY TEST DATA

 

Material E7001         Color : BLACK         Date : 20070201                        

Press Cure   Sheet: 12 min  170     Button: 30  min 160          O-RING:      S     

Post Cure    Sheet:   min          Button:    min              O-RING:     min    

Customer:                         TEL:0592-6313227           FAX:0592-6313223

 

SPECIFICATION:  M2BA710A14B13EA14F17 (Z1=70±5  )
* ITEM

REQUIRED

TEST DATA

* Original Property

Hardness, shore A,  Pts

70±5

73

Specific Gravity ,  g/cm3

 

 

Modulus,  %,psi

 

 

Tensile strength ,  N/mm2

10

14.7

Elongation,  %

300

328

* A 14 Heat Aged ,  ASTM  D 573  70 Hrs  at 100

Hardness Change ,  Pts

±15

+1

Tensile Strength Change ,  %

±30

-8.2

Elongation Change ,  %

-50

-31.3

* B 13 Compression Set , ASTM D395  Method B  22Hrs  at 70

Deflection ,  %

50

13

*C  Ozone Resistance, _____pphm ____h  at ____

 

 

*EA14 Water Resistance , ASTM  D471  70 Hrs  at100

Hardness Change ,  Pts

 

-1

Volume Change ,  %

10

+0.7

Elongation Change ,  %

 

 

Tensile Strength Change ,  %

 

 

*EF  Fluid Resistance, Ref. Fuel A , ASTM  D471   Hrs  at

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*EF   Fluid Resistance, Ref. Fuel B , ASTM  D471    Hrs  at 

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*EO  Fluid Resistance, ASTM # 1 oil ,  ASTM  D471     Hrs  at    

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*EO  Fluid Resistance, ASTM # 3 oil ,  ASTM  D471    Hrs  at   

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*F17 Low-temperature nonbrittle after 3_min at -40

PASS

PASS

 

Engineer:                      Plant Manager: ____

 

 

XIAMEN HAIYIXIN RUBBER SEAL CO;LTD

PHYSICAL  PROPERTY  TEST  DATA

 

Material   SIL5001       Color :  BRU          Date : 20070201                         

Press Cure   Sheet: 12  min 170     Button:  30 min 160         O-RING:      S     

Post Cure    Sheet: 240 min 200    Button:  240 min 200         O-RING:     min    

Customer:                         TEL:0592-6313227           FAX:0592-6313223

 

SPECIFICATION:ASTM D2000  5GE508A19B37EO36C12F19G11                        
* ITEM

REQUIRED

TEST DATA

* Original Property

 Hardness, shore-A,  Pts

50+/-5

50

Specific Gravity ,  g/cm3

 

1.15

Modulus,    %,psi

 

213

Tensile strength , min, psi

800

1198

Elongation,min ,%

250

420

* A 19 Heat Aged ,  ASTM  D 573    70 Hrs  at   225

Hardness Change ,  Pts

+10

+1

Tensile Strength Change , max, %

-25

-15.2

Elongation Change ,  max,%

-30

+8.2

* B 37 Compression Set , ASTM D395  Method B  22 Hrs  at  175

Deflection ,  %

25

15.8

*C 12 Ozone Resistance,  50 pphm 72 h  at 40

 

NO crack

*EA  Water Resistance , ASTM  D471      Hrs  at   

Hardness Change ,  Pts

 

 

Volume Change ,  %

 

 

Elongation Change ,  %

 

 

Tensile Strength Change ,  %

 

 

*EF  Fluid Resistance, Ref. Fuel C, ASTM  D471       Hrs  at     

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*EF  Fluid Resistance, Ref. Fuel B , ASTM  D471       Hrs  at   

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*EO  Fluid Resistance, ASTM # 1 oil ,  ASTM  D471    Hrs  at    

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change , max,%

 

 

Volume Change , max, %

 

 

*EO 36 Fluid Resistance, ASTM # 3 oil ,  ASTM  D471    70 Hrs  at 150

Hardness Change ,  Pts

-30

-19.8

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

+60

+53.4

*F19Low-temperature nonbrittle after 3min at55

 

pass

*G 11 Tear  resistance  ASTM D624 DieB

 

18.3KN/m

 

Engineer:                      Plant Manager: _____

 

 

XIAMEN HAIYIXIN RUBBER SEAL CO;LTD

PHYSICAL    PROPERTY  TEST  DATA

 

Material   V7001        Color :   BLACK       Date : 20070201                        

Press Cure   Sheet: 12  min 170     Button:  30 min 160          O-RING:      S     

Post Cure    Sheet: 1440 min  230   Button:  1440min 230        O-RING:     min    

Customer:                         TEL:0592-6313227           FAX:0592-6313223

 

SPECIFICATION:ASTM D2000 M2HK810A1-10B38EF31EO78F15                      
* ITEM

REQUIRED

TEST DATA

* Original Property

 Hardness, Shore-A,  Pts

70+/-5

73

Specific Gravity ,  g/cm3

 

1.86

Modulus,  100 %,Mpa

 

7.3

Tensile strength , min, MPa

10

14.5

Elongation,min ,%

150

215

* A1-10 Heat Aged ,  ASTM  D 573    70 Hrs  at  250

Hardness Change ,  Pts

+10

+3

Tensile Strength Change , max, %

-25

-6.0

Elongation Change ,  max,%

-25

-2.6

* B 38 Compression Set , ASTM D395  Method B  22 Hrs  at  200

Deflection ,  %

50

22.3

*C  Ozone Resistance, _____pphm ____h  at ____

 

 

*EA  Water Resistance , ASTM  D471      Hrs  at   

Hardness Change ,  Pts

 

 

Volume Change ,  %

 

 

Elongation Change ,  %

 

 

Tensile Strength Change ,  %

 

 

*EF 31 Fluid Resistance, Ref. Fuel C, ASTM  D471     70 Hrs  at  23

Hardness Change ,  Pts

+/-5

+1

Tensile Strength Change ,  %

-25

-8.2

Elongation Change ,  %

-20

+2.7

Volume Change ,  %

0~+10

+2.0

*EF  Fluid Resistance, Ref. Fuel B , ASTM  D471       Hrs  at   

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*EO 78 Fluid Resistance, ASTM # 1 oil ,  ASTM  D471   70 Hrs  at  200

Hardness Change ,  Pts

-15~+5

-2

Tensile Strength Change ,  %

-40

-7.7

Elongation Change , max,%

-20

+5.3

Volume Change , max, %

0~+15

+10.2

*EO  Fluid Resistance, ASTM # 3 oil ,  ASTM  D471        Hrs  at   

Hardness Change ,  Pts

 

 

Tensile Strength Change ,  %

 

 

Elongation Change ,  %

 

 

Volume Change ,  %

 

 

*F15 Low-temperature nonbrittle after 3min at -25

PASS

PASS

 

Engineer:                        Plant Manager: _____

 

 

 

 
© 2007 版权所有:厦门网上乐百家百有限公司                          邮    编:325000
地    址:厦门市海沧东孚洪塘龙井社                          
电    话:0592-6313225 6313227                                      传    真:0592-6313223